Strip - Durimphy® - Ni18Co9Mo5Ti0 pages
Cold Rolled Strip
Durimphy
Durimphy is a structured hardening maraging type martensitic alloy. Durimphy has a very high yield strength, is hardened by
ageing treatment (3 hours at 480° without any dim ensional change and has a very good fatigue resistance. Main
C)
applications are springs for watch industry, springs for various applications, belts for CVT transmission, rocket fins.
Chemical Composition (% weight)
Ni
Co
Mo
Ti
Fe
18
9
5
0,5
Bal
Physical properties
Density
(g/cm³)
8,1
Coefficient of Thermal
Expansion between 20
and 100°
C
-6
-1
(10 .° )
C
9,5
Melting T°
(°
C)
1430 / 1460
Resistivity at 20°C
(µΩ.cm)
Thermal
conductivity
(W/(°
Cm))
Specific heat at 20°
C
-1
-1
C
(J.Kg .° )
44
14,7
460
Mechanical properties (Typical values)
Annealed
Annealed +
ageing treatment
(3h/480°
C)
TS
(MPa)
1020
YS
(MPa)
980
1880
1860
El
(%)
7
TS
Hardness
(HV)
320
4
AFTER AGEING TREATMENT 3h AT 480°
C
TS (MPa) - YS (MPa)
Condition
2500
570
YS
2000
1500
TS
DELIVERY STATE
YS
1000
500
Durimphy can also be delivered in the hard condition when
higher mechanical properties are necessary, upon request
0
20
40
60
80
100
Degree of cold work (%)
Standard delivery form & dimensions
Form *
Thickness (mm)
Width* (mm)
Length (mm)
Temper
Coil - Sheet
0,05 to 1,5
10 to 580
500 to 3500
Annealed
0,050 to 0,50
10 to 90
-
Hard
Coil
* Depending on thickness
The data enclosed in this document are only given as indicative values and correspond to our standard product. Different specific requirement are
subject to discussion and formal approval by Aperam Alloys Imphy. For further information or special request, please contact us.
Aperam Alloys Imphy
B.P. 1
Avenue Jean Jaurès
F- 58160 Imphy
Tel + 33 3 86 21 30 00
Fax + 33 3 86 21 31 00
nickel.alloys@aperam.com
www.aperam.com/alloys-imphy
© June 2012
__________________________________________________________
"